Stability of flexible thin-film metallization stimulation electrodes: analysis of explants after first-in-human study and improvement of in vivo performance - Inria EPFL Access content directly
Journal Articles Journal of Neural Engineering Year : 2020

Stability of flexible thin-film metallization stimulation electrodes: analysis of explants after first-in-human study and improvement of in vivo performance

Silvestro Micera
Ken Yoshida
  • Function : Author
Jean-Louis Divoux
  • Function : Author
  • PersonId : 915627

Abstract

Objective. Micro-fabricated neural interfaces based on polyimide (PI) are achieving increasing importance in translational research. The ability to produce well-defined micro-structures with properties that include chemical inertness, mechanical flexibility and low water uptake are key advantages for these devices. Approach. This paper reports the development of the transverse intrafascicular multichannel electrode (TIME) used to deliver intraneural sensory feedback to an upper-limb amputee in combination with a sensorized hand prosthesis. A failure mode analysis on the explanted devices was performed after a first-inhuman study limited to 30 d. Main results. About 90% of the stimulation contact sites of the TIMEs maintained electrical functionality and stability during the full implant period. However, optical analysis post-explantation revealed that 62.5% of the stimulation contacts showed signs of delamination at the metallization-PI interface. Such damage likely occurred due to handling during explantation and subsequent analysis, since a significant change in impedance was not observed in vivo. Nevertheless, whereas device integrity is mandatory for long-term functionality in chronic implantation, measures to increase the bonding strength of the metallization-PI interface deserve further investigation. We report here that silicon carbide (SiC) is an effective adhesion-promoting layer resisting heavy electrical stimulation conditions within a rodent animal trial. Optical analysis of the new electrodes revealed that the metallization remained unaltered after delivering over 14 million pulses in vivo without signs of delamination at the metallization-PI interface. Significance. Failure mode analysis guided implant © 2020 IOP Publishing Ltd J. Neural Eng. 17 (2020) 046006 PČvančara et al stability optimization. Reliable adhesion of thin-film metallization to substrate has been proven using SiC, improving the potential transfer of micro-fabricated neural electrodes for chronic clinical applications. (Document number of Ethical Committee: P/905/CE/2012; Date of approval: 2012-10-04)
Fichier principal
Vignette du fichier
2020_J._Neural_Eng.pdf (4.08 Mo) Télécharger le fichier
Origin : Publisher files allowed on an open archive
Loading...

Dates and versions

hal-02907515 , version 1 (28-07-2020)

Licence

Attribution

Identifiers

Cite

Paul Čvančara, Tim Boretius, Víctor López-Álvarez, Pawel Maciejasz, David Andreu, et al.. Stability of flexible thin-film metallization stimulation electrodes: analysis of explants after first-in-human study and improvement of in vivo performance. Journal of Neural Engineering, 2020, 17 (4), pp.#046006. ⟨10.1088/1741-2552/ab9a9a⟩. ⟨hal-02907515⟩
80 View
209 Download

Altmetric

Share

Gmail Facebook X LinkedIn More